[硼对AZ91镁合金显微组织和腐蚀性能的影响]镁合金金相腐蚀液
时间：2019-05-02 03:29:45 来源：柠檬阅读网 本文已影响 人 
摘要： 研究了B含量对AZ91镁合金显微组织和腐蚀性能的影响。结果表明：B元素的引入明显细化了镁合金的组织，随着B含量的增加，合金中α-Mg相和β的尺寸减小，β相由原来连续的网状分布变为断续、离散的岛屿状分布。同时，B的加入可以有效的提高镁合金的耐腐蚀性能。
Abstract: The impact of B content on the corrosion resistance and microstructure of AZ91 magnesium alloy was studied. The results show as following: the introduction of element of B refines microstructure of magnesium alloy obviously, and along with increasing B content, the size of α-Mg phase and β in the alloy reduce, and β phase becomes discontinuous, discrete island-like distribution from the continuous reticular distribution. Meanwhile, the mix of B can effectively improve the corrosion resistance of magnesium alloy.
关键词： 镁合金；显微组织；腐蚀性能
Key words: magnesium alloy；microstructure；corrosion resistance
中图分类号：TG13文献标识码：A文章编号：1006-4311（2012）09-0023-02